Zirconia est materia magna vi mechanica et fractura spissitudo in locus temperatus. Nostra zirconia (ZrO2) cum 3mol%Y2O3 zirconia stabili partiali additur (PSZ). Quia particula diametri PSZ materialis parva est, magna praecisione discursum est, et applicatio eius ad amussim machinarum partium sicut formas dilatatur. Praeterea adhiberi possunt etiam instrumenta industrialia, partes connectoris opticae et instrumenti medii comminuendi. Alta fractura durities PSZ ad fontes speciales adhiberi potest, et etiam late in cultris ceramicis domesticis, scalpro et aliis partibus adhibetur.
Materia Properties
| Item | 95% Alumina | 99% Alumina | Zirconia | Pii carbide | PiiNitride | aluminiumNitride | Machinabilis tellus |
| Color | album | Lumen flavum | album | nigrum | nigrum | griseo | album |
| Densitas (g/cm3) | 3.7g/cm3 | 3.9g/cm3 | 6.02g/cm3 | 3.2g/cm3 | 3.25g/cm3 | 3.2g/cm3 | 2.48g/cm3 |
| Absorptio aquae | 0% | 0% | 0% | 0% | 0% | 0% | 0% |
| Duritia (HV) | 23.7 | 23.7 | 16.5 | 33 | 20 | - | - |
| Flexurae fortitudo (MPa) | 300MPa | 400MPa | 1100MPa | 450MPa | 800MPa | 310MPa | 91MPa |
| Fortitudo compressive (MPa) | 2500MPa | 2800MPa | 3600MPa | 2000MPa | 2600MPa | - | 340MPa |
| Young's Modulus Elasticitas | 300GPa | 300GPa | 320GPa | 450GPa | 290GPa | 310~ 350GPa | 65GPa |
| Poisson's Ratio | 0.23 | 0.23 | 0.25 | 0.14 | 0.24 | 0.24 | 0.29 |
| Scelerisque Conductivity | 20W/m°C | 32W/m°C | 3W/m°C | 50W/m°C | 25W/m°C | 150W/m°C | 1.46W/m°C |
| Dieelectrica Fortitudo | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm | 14KV/mm |
| Volumen Resistentia(25℃) | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm | >105Ω·cm | >1014Ω·cm | >1014Ω·cm | >1014Ω·cm |
Zirconia (ZrO2) I principalis usus
Finge et fingo instrumenta (variae formae, praecisio positio fixture, velit fixtura); Molendinum partes (classificans, aeris fluunt molendinum, molendinum molendinum); Instrumentum industriae (cutter industrialis, machina rima, volumen prelo plana); Connexoris partium opticarum (anulum obsignans, manica, fixtura V sulcus); Fons proprius (coil fons, lamella ver); Dolor productorum (parvus insulatus solus, cultellus ceramic, scalper).